Title: |
Closed Field Unbalanced Magnetron Sputtering Ion Plating of DLC and Si-DLC Films onto Nitrile Rubber |
Authors: |
M. Lubwama, B. Corcoran, K. Sayers, J.B. Kirabira, A. Sebbit |
Keywords: | DLC film; Magnetron sputtering; Raman spectroscopy |
Issue Date: | August 29th – 30th, 2012 |
Abstract: | In this study, diamond-like carbon (DLC) and Silicon doped DLC (Si-DLC) have been deposited on acrylonitrile butadiene rubber (NBR rubber) via a closed field unbalanced magnetron sputtering ion plating (CFUBMSIP) system at a bias voltage of − 30V. Comparison was made for DLC and Si-DLC films deposited with and without a Si-C interlayer. A sputter cleaning system was integrated into the deposition process so as to have no time for recontamination between the cleaning and deposition stages. The results show the presence of a micro-crack like network of the films on NBR rubber. A non-columnar coating is formed that promoted the generally good adhesion between the films and the NBR substrate. For films with Si-C interlayer an adhesion rating of 4A is observed. The composite micro-hardness was highest for DLC films at 15.5 GPa for an indentation load of 147.1 mN. The inclusion of the Si-C interlayer generally tended to increase the intensity ratio (ID/IG) for both DLC and Si-DLC films. The increase in the sp2 content was a result of the Si-C interlayer. The hybridization of carbon in terms of sp2 and sp3 bonding was used to explain these results. This study is motivated by the potential of applying DLC and Si-DLC films onto actual piston seals used in handpumps for rural water supply in sub-Saharan Africa. |
Published in: | Proceedings of the 29th International Manufacturer’s Conference (IMC29), August 29th – 30th, 2012, Belfast, UK |
Attachments
Attachment Name | Attachment Type | ||
Closed Field Unbalanced Magnetron Sputtering Ion Plating of DLC and Si-DLC Films onto Nitrile Rubber | DOC | PS |